| Common Name | Density | Yield Strength | Ultimate Strength | Shear Strength | Flexural Strength | Elastic Modulus | Shear Modulus | Flexural Modulus | Poissons Ratio | Hardness | Elongation at Break | Elongation at Yield |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| g/cc | MPa | MPa | MPa | MPa | GPa | GPa | GPa | % | % | |||
| Acetal Homopolymer | 1.41 | 66 | 69 | 52 | 75 | 3 | 2.9 | 0.37 | 95SD | 40 | 21 | |
| Bronze 544-H04 | 8.89 | 395 | 470 | 103 | 39 | 0.321 | 40HRB | 20 | ||||
| Aluminum 6061-T6 | 2.7 | 276 | 310 | 207 | 68.9 | 26 | 0.33 | 60HRB | 17 | |||
| LDPE | 0.921 | 11 | 10.8 | 74.6 | 0.219 | 0.264 | 48.6SD | 322 | 28.9 | |||
| Steel 1020 (mild steel) | 7.87 | 350 | 420 | 186 | 72 | 0.29 | 68HRB | 15 | ||||
| Stainless 440C, full hard | 7.8 | 1280 | 1750 | 200 | 0.283 | 58HRC | 4 |